This paper prepared a new kind of carbon dots-polyvinyl alcohol-carboxymethyl cellulose composite film with antibacterial properties. Carbon dots and citric acid were used as cross-linking agents, and polyvinyl alcohol and carboxymethyl cellulose were used as matrices respectively. The mechanical properties, UV shielding performance, thermal stability, antioxidant capability, and antibacterial activities of the carbon dots-polyvinyl alcohol-carboxymethyl cellulose composite film were researched. The prepared carbon dots-polyvinyl alcohol-carboxymethyl cellulose composite film was applied in the strawberry freshness preservation test. And test results indicated that the carbon dots-polyvinyl alcohol-carboxymethyl cellulose composite film could prevent rotting and extend the shelf life of strawberries. This carbon dots-polyvinyl alcohol-carboxymethyl cellulose composite film could be applied in the food active packaging field.

ABSTRACT: From a pollination biology standpoint, this study compared modifications in the flowering phenology, soluble sugar and protein content of pollen, antioxidant enzyme system, and storage traits of five cultivated populations of Paeonia ostii ‘Feng dan’ at various altitudes in Luoyang. The findings indicated that the first blooming phase was delayed at greater altitudes. There was a significant difference in the soluble sugar content of pollen between sites; and there was no discernible relationship between soluble sugar content and altitude. With increasing altitude, there is a tendency for soluble protein content to decrease. The activities of antioxidant enzymes in pollen from cultivated populations at varying altitudes showed SOD and POD enzyme activities generally increasing with decreasing temperature, whereas CAT enzymes showed divergent patterns. Differences existed in the storage time of pollen across populations at different altitudes, and pollen from higher altitudes appeared to be better adapted to low-temperature storage environments. The rate of decrease in pollen viability under dry storage at -74.7 °C was significantly lower than under other storage conditions. The comprehensive analysis concludes that the variations in ‘Feng dan’ cultivation populations within the same region at different altitude zones can be leveraged for cross-pollination among proximate populations, utilizing low-temperature dry pollen storage technology, with the aim of achieving abundant oil peony production.

ABSTRACT The wide use of poly(propylene carbonate) (PPC), a biodegradable polymer made from carbon dioxide, will contribute greatly to alleviating environmental issues such as white pollution and greenhouse effect. However, the poor mechanical properties and low glass transition temperature (T g ) seriously limit the practical application of PPC. Traditional reinforcement methods for PPC will reduce the toughness sharply. Herein, we propose a new strategy for preparing strong and tough PPC through in situ generated high‐performance PPC‐based cross‐linked microdomains (PPC‐MD). Specifically, based on the aminolysis reaction between carbonate groups in PPC and multiple amine groups in polyethylenimine, PPC‐MD and hydroxy‐terminated PPC with low molecular weight (l‐PPC‐OH) are generated during melt blending. Then, hexamethylene diisocyanate is added to link l‐PPC‐OH for the purpose of eliminating the plasticization of l‐PPC‐OH and the degradation effect of terminal hydroxyl group. The PPC‐MD with high T g can effectively reinforce PPC and improve its toughness. The PPC/PEI/HDI‐0.02/0.04 shows a high tensile strength of 29.4 ± 2.5 MPa and a toughness of 86.8 ± 5.2 MJ/m 3 , which is 2.58‐ and 1.38‐folds of PPC, respectively. Besides, the PPC‐MD can greatly improve the T g of PPC as well. It is worth highlighting that this method can be accomplished by melt blending, which is facile and can be scaled up. We envision that this work will enrich the modification method of PPC and promote the practical application of PPC as the as‐fabricated PPC shows integrated high strength, high toughness, and high T g .