Abstract Hydrogen‐based energy is a promising renewable and clean resource. Thus, hydrogen selective microporous membranes with high performance and high stability are demanded. Novel NH 2 ‐MIL‐53(Al) membranes are evaluated for hydrogen separation for this goal. Continuous NH 2 ‐MIL‐53(Al) membranes have been prepared successfully on macroporous glass frit discs assisted with colloidal seeds. The gas sorption ability of NH 2 ‐MIL‐53(Al) materials is studied by gas adsorption measurement. The isosteric heats of adsorption in a sequence of CO 2 &gt; N 2 &gt; CH 4 ≈ H 2 indicates different interactions between NH 2 ‐MIL‐53(Al) framework and these gases. As‐prepared membranes are measured by single and binary gas permeation at different temperatures. The results of singe gas permeation show a decreasing permeance in an order of H 2 &gt; CH 4 &gt; N 2 &gt; CO 2 , suggesting that the diffusion and adsorption properties make significant contributions in the gas permeation through the membrane. In binary gas permeation, the NH 2 ‐MIL‐53(Al) membrane shows high selectivity for H 2 with separation factors of 20.7, 23.9 and 30.9 at room temperature (288 K) for H 2 over CH 4 , N 2 and CO 2 , respectively. In comparison to single gas permeation, a slightly higher separation factor is obtained due to the competitive adsorption effect between the gases in the porous MOF membrane. Additionally, the NH 2 ‐MIL‐53(Al) membrane exhibits very high permeance for H 2 in the mixtures separation (above 1.5 × 10 −6 mol m −2 s −1 Pa −1 ) due to its large cavity, resulting in a very high separation power. The details of the temperature effect on the permeances of H 2 over other gases are investigated from 288 to 353 K. The supported NH 2 ‐MIL‐53(Al) membranes with high hydrogen separation power possess high stability, resistance to cracking, temperature cycling and show high reproducibility, necessary for the potential application to hydrogen recycling.

Hydrogen Selective NH2‐MIL‐53(Al) MOF Membranes with High Permeability