Abstract This study explores the synthesis and characterization of zinc molybdate (ZnMoO 4 ) nanosheets with emphasis on their potential application for energy storage devices particularly supercapacitors. The synthesis of ZnMoO 4 nanosheets was done through co-precipitation followed by examination of their structure, morphology, optical, thermal behaviour and electrochemical performance by various characterization techniques. X-ray diffraction (XRD) analysis confirmed that the formation of monoclinic ZnMoO 4 phase with the average crystallite size 17.93 nm. Scanning electron microscopy (SEM) and Transmission electron microscopy (TEM) revealed that this material had nanosheets-like structure which helps to increase ion transport and surface area; these two factors are essential for enhancing the material’s supercapacitor efficacy. The semiconductor characteristics were determined using UV–Visible diffuse reflectance spectroscopy (UV-DRS) which indicated a band gap energy of 4.2 eV. Fourier transform infrared (FTIR) analysis confirmed that the presence of Zn–O and Mo–O bonds in their crystal lattice. Thermogravimetric analysis (TGA) showed that the ZnMoO 4 nanosheets had thermal stability since they experienced only a slight mass loss of 2.57 % up to 800 °C. Cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) tests were undertaken to find out the specific capacitance and the value is 618 F g⁻ 1 at a current density of 1 A g⁻ 1 .

Facile synthesis and characterization of zinc molybdate (ZnMoO4) nanosheets for electrochemical supercapacitor application