Abstract

Purpose This paper aims to conduct work to obtain high-quality brazed joint of YAG ceramic and kovar alloy. Design/methodology/approach Wetting and spreading behavior of AgCuTi filler alloy on YAG ceramic and kovar alloy under vacuum (2∼3 × 10–4 Pa) and argon conditions was investigated and compared. Then, YAG ceramic was brazed to kovar alloy under a high vacuum of 2∼3 × 10–4 Pa; the influence of holding time on the interface structure of the joint was investigated. Findings The wettability of AgCuTi on YAG is poor in the argon atmosphere, the high oxygen content in the reaction layer hinders the formation of the TiY2O5 reaction layer, thereby impeding the wetting of AgCuTi on YAG; in the vacuum, a contact angle (?=16.6°) is obtained by wetting AgCuTi filler alloy on the YAG substrate; the microstructure of the YAG/AgCuTi/kovar brazed joint is characterized to be YAG/Y2O3/(Fe, Ni)Ti/Ag(s, s) + Cu(s, s)/Fe2Ti + Ni3Ti/Fe2Ti/kovar; at 870 °C for the holding time of 10 min, a (Fe, Ni) Ti layer of approximately 1.8 µm is formed on the YAG side. Originality/value Wetting and spreading behavior of the brazing filler alloy under different conditions and the influence of the holding time on the interface microstructure of the joint were studied to provide references for obtaining high-quality brazed joints.