Experiment and numerical analysis were conducted in this study to reveal the residual resistant capacity of the cold-formed Q1100 ultra-high strength steel (UHSS) channel section stub column with grooving corrosion. Based on the results of tensile coupon test, the strength properties of the Q1100 UHSS were barely changed by the cold-forming process. A clear reduction in the ductile properties was observed, after the cold-forming process. The load-end shortening curve of the cold-formed Q1100 UHSS channel section stub columns with different grooving corrosions were obtained through the axial compressive experiment. The initial resistant stiffness was reduced by the grooving corrosion significantly, because of the reduction in the cross-section area. Decrease in the corrosion angle and increment in the corrosion length enhanced the adverse effects of grooving corrosion on the resistant capacity. Local buckling was observed in the flange and web. The flanges near the corrosion weakening area were more prone to local buckling, because of the stress transfer from web to flange. A numerical modelling method was proposed to simulate the resistant performance of the cold-formed Q1100 UHSS channel section stub columns with different grooving corrosions, which was validated by the comparison in load-end shortening curve, ultimate resistance and failure mode. Effects of corrosion angle, corrosion length, and corrosion location on the resistant capacity and failure mode were investigated through the parametric study. Compared with corrosion location, the corrosion angle and corrosion length exhibited more significant effects on the resistant capacity of the cold-formed Q1100 UHSS channel section stub columns.

To investigate the effect of combined end-and-shaft post-grouting on the vertical load-bearing performance of bridge-bored piles in the Dongting Lake area of Hunan, two post-grouted piles were subjected to bi-directional O-cell and top-down load tests before and after combined end-and-shaft grouting, based on the Wushi to Yiyang Expressway project. A comparative analysis was conducted on the bearing capacity, deformation characteristics, and load transfer behavior of the piles before and after grouting. This study also examined the conversion coefficient γ values of different soil layers obtained from the bi-directional O-cell test for bearing capacity calculations. Additionally, the characteristic values of the end bearing capacity, obtained from the bi-directional O-cell and top-down load tests, were compared with the values calculated using the relevant formulas in the current standards, which validated the accuracy of existing regulations and traditional loading methods. The results indicate that the stress distribution along the pile shaft differed between the two test methods. In the bi-directional O-cell test, the side resistance developed from the end to the head, while in the top-down load test, it developed from the head to the end. After combined post-grouting, the ultimate bearing capacity of the piles significantly increased, with side resistance increasing by up to 81.03% and end resistance by up to 105.66%. The conversion coefficients for the side resistance in silty sand and gravel before and after grouting are 0.86 and 0.80 and 0.81 and 0.69, respectively. The characteristic values of the end bearing capacity, as measured by the bi-directional O-cell and top-down load tests, were substantially higher than those calculated using the current highway bridge and culvert standards, showing increases of 133.63% and 86.15%, respectively. These findings suggest that the current standard formulas are overly conservative. Additionally, the measured values from the top-down load test may underestimate the actual bearing capacity of piles in engineering projects. Therefore, it is recommended that future pile foundation designs incorporate both bi-directional O-cell testing and combined post-grouting techniques to optimize design solutions.