The economic and safety issues caused by ice accretion have become more and more serious. Except for traditional ways of anti‐icing, such as spraying agents, mechanical/thermal removal, etc., more economic approaches are urgently required. This work demonstrates the conceptual feasibility of using a self‐lubricated photothermal coating for both anti‐icing and deicing function. The coating is generally water repellent and infiltrated with hydrocarbon or perfluorocarbon oils as the lubricant to endow a liquid interface for preventing ice accumulation and minimizing the adhesion of ice on surfaces once it is formed. Fe 3 O 4 nanoparticles are added to the film to afford high efficiency photothermal effect under near‐infrared irradiation for rapidly melting the accumulated ice. The conceptual strategy can be easily implemented as a facile method to fabricate analogous sprayed coatings. It represents a major advance to tackle the challenging icing issue that is normally seen as a disaster in everyday life.

Amorphous W-S-C-N lubricating films were prepared by sputtering two WS2 targets and an additional WC target in Ar&N2 atmosphere. The W-S-C-N film demonstrated a notably stable low coefficient of friction (COF) of approximately 0.01, as well as a wear rate of 1.50 × 10-7 mm3/Nm over extended sliding cycles. These characteristics indicated superior tribological properties compared to the deposited WS2, W-S-C, and W-S-N films. The formation of the friction-induced well-crystallized WS2 transfer film with its (002) basal plane parallel to the sliding surface of the counterpart ball contributed to the low friction of the W-S-C-N film. Furthermore, the embedded amorphous and nanocrystalline WC phase within the crystallized WS2-based transfer film further enhanced the stability and durability of the transfer film.