Waste printed circuit boards (WPCBs) are considered as the most complex and valuable part of the discarded mobile phone. Alkaline slurry electrolysis is certified as an effective method to recover copper from WPCBs of mobile phones (WPCB-MPs). To promote its industrial application, 5000 mL scale trials were conducted and the results show that: Electrolysis at 30 g/L WPCB-MPs, 25 g/L Cu2+(CuSO4·5H2O), 4 mol/L NH3·H2O, 0.5 mol/L NaCl, 0.5 mol/L NH4Cl, 20 mA/cm2 and 298 K for 8 h, the current efficiency is 90.47 %, the copper recovery is 92.04 %, and the purity of cathode copper is 99.79 %. Electrolyte circulation hardly affected current efficiency, copper recovery rate and copper purity, which were higher than 90 %, 90 %, and 99 %, respectively. The semi-scaled experiment demonstrates its feasibility in industrial application. Primarily cost analysis shows that producing a ton of cathode copper has a profit of about $5,144.5. Therefore, alkaline slurry electrolysis has a broad industrial prospect in WPCBs recycling.

Lithium is an important alkalinous metal with a wide range of usage and high economic value. With the transformation of the global energy structure and the rapid development of a new energy industry, the demand for lithium is increasing. Therefore, it is of great strategic significance and economic value to find new ways to obtain lithium resources. The total amount of secondary lithium resources is abundant, but the current research mainly focuses on lithium extraction from waste lithium-ion batteries (LIBs), rather than the waste resources generated during LIB production. Therefore, in this study, the sludge generated during the production of lithium iron phosphate batteries (LiFePO4, LFP) is used as a raw material to extract lithium using the leaching system of H2SO4–H2O2, and factors that impact the leaching efficiency are discussed. The results show that the leaching efficiency of lithium could reach 99.32% under optimal experimental conditions. Thermodynamic and kinetic analyses indicate that lithium sludge leaching by sulfuric acid can occur spontaneously at room temperature, and the leaching process is controlled by a combination of chemical reaction and diffusion. The research results provide a new approach for lithium supply, showing a good perspective.