High pressure provides a unique tuning method depending on structure modulation to explore the structure–property relationship. Herein, the pressure‐induced structural phase transformation and enhanced superconductivity in a layered binary phosphide Sn 4 P 3 are reported. Comprehensive measurements using in situ synchrotron X‐Ray diffraction and Raman spectroscopy reveal a structural phase transition with mild distortion of SnP 3 building blocks and interlayer shrinkage under high pressure. This differs from a conventional trigonal SnAs(P) 3 to square SnAs(P) 4 topotactic transition in SnAs(P)‐based compound. Through this structure reconstruction under high pressure, electron distribution has been reorganized and phonons have softened, facilitating a high superconducting temperature ( T c ) value of 7.8 K at 34.9 GPa, which is almost six times higher than its ambient value. The study introduces a new transition route in layered SnAs/SnP‐based intermetallic materials and provides insight into the structural and electronic changes under high pressure for Sn 4 P 3 .