For the first time, stable aqueous dispersions of polymer-coated graphitic nanoplatelets can be prepared via an exfoliation/in-situ reduction of graphite oxide in the presence of poly(sodium 4-styrenesulfonate).

Significant enhancement in mechanical stiffness (10–200%) and fracture strength (∼50%) of graphene oxide paper, a novel paperlike material made from individual graphene oxide sheets, can be achieved upon modification with a small amount (less than 1 wt %) of Mg2+ and Ca2+. These results can be readily rationalized in terms of the chemical interactions between the functional groups of the graphene oxide sheets and the divalent metals ions. While oxygen functional groups on the basal planes of the sheets and the carboxylate groups on the edges can both bond to Mg2+ and Ca2+, the main contribution to mechanical enhancement of the paper comes from the latter.

We have synthesized, characterized, and computationally simulated/validated the behavior of two new metal–organic framework (MOF) materials displaying the highest experimental Brunauer–Emmett–Teller (BET) surface areas of any porous materials reported to date (∼7000 m2/g). Key to evacuating the initially solvent-filled materials without pore collapse, and thereby accessing the ultrahigh areas, is the use of a supercritical CO2 activation technique. Additionally, we demonstrate computationally that by shifting from phenyl groups to "space efficient" acetylene moieties as linker expansion units, the hypothetical maximum surface area for a MOF material is substantially greater than previously envisioned (∼14600 m2/g (or greater) versus ∼10500 m2/g).

ADVERTISEMENT RETURN TO ISSUEPREVArticleNEXTRing-opening metathesis polymerization (ROMP) of norbornene by a Group VIII carbene complex in protic mediaSonBinh T. Nguyen, Lynda K. Johnson, Robert H. Grubbs, and Joseph W. ZillerCite this: J. Am. Chem. Soc. 1992, 114, 10, 3974–3975Publication Date (Print):May 1, 1992Publication History Published online1 May 2002Published inissue 1 May 1992https://pubs.acs.org/doi/10.1021/ja00036a053https://doi.org/10.1021/ja00036a053research-articleACS PublicationsRequest reuse permissionsArticle Views11208Altmetric-Citations904LEARN ABOUT THESE METRICSArticle Views are the COUNTER-compliant sum of full text article downloads since November 2008 (both PDF and HTML) across all institutions and individuals. These metrics are regularly updated to reflect usage leading up to the last few days.Citations are the number of other articles citing this article, calculated by Crossref and updated daily. Find more information about Crossref citation counts.The Altmetric Attention Score is a quantitative measure of the attention that a research article has received online. Clicking on the donut icon will load a page at altmetric.com with additional details about the score and the social media presence for the given article. Find more information on the Altmetric Attention Score and how the score is calculated. Share Add toView InAdd Full Text with ReferenceAdd Description ExportRISCitationCitation and abstractCitation and referencesMore Options Share onFacebookTwitterWechatLinked InRedditEmail Other access optionsGet e-AlertscloseSupporting Info (1)»Supporting Information Supporting Information Get e-Alerts

A new microporous metal-organic framework compound featuring chiral (salen)Mn struts is highly effective as an asymmetric catalyst for olefin epoxidation, yielding enantiomeric excesses that rival those of the free molecular analogue. Framework confinement of the manganese salen entity enhances catalyst stability, imparts substrate size selectivity, and permits catalyst separation and reuse.