We have developed a facile, scale up, and efficient method for the preparation of graphitic-C3N4 nanofibers (GCNNFs) as electrodes for supercapacitors and photocatalysts. The as-synthesized GCNNFs have 1D structure with higher concentration of nitrogen that is favorable for higher conductivity and electrochemical performance. Secondly, the high surface area of GCNNF provides a large electrode-electrolyte contact area, sufficient light harvesting and mass transfer, as well as increased redox potential. Thus, the GCNNF supercapacitor electrode shows high capacitance of 263.75 F g(-1) and excellent cyclic stability in 0.1 M Na2SO4 aqueous electrolyte with the capacitance retention of 93.6% after 2000 cycles at 1 A g(-1) current density. GCNNFs exhibit high capacitance of 208 F g(-1) even at 10 A g(-1), with the appreciable capacitance retention of 89.5%, which proves its better rate capability. Moreover, the GCNNF shows enhanced photocatalytic activity in the photodegradation of RhB in comparison to the bulk graphitic-C3N4 (GCN). The degradation rate constant of GCNNF photocatalyst is almost 4 times higher than GCN. The enhanced photocatalytic activity of GCNNF is mainly due to the higher surface area, appropriate bandgap, and fewer defects in GCNNF as compared to GCN. As an economical precursor (melamine) and harmless, facile, and template-free synthesis method with excellent performance both in supercapacitors and in photodegradation, GCNNF is a strong candidate for energy storage and environment protection applications.

We have established a facile and scaleable approach to fabricate tubular graphitic-C3N4 using melamine. The construction of the unique tubular morphology is a result of the pre-treatment of melamine with HNO3. Herein, for the first time, we have explored the electrochemical properties of g-C3N4 as an electrode material for supercapacitors. Tubular g-C3N4 has significant advantages due to its distinctive morphology, high surface area (182.61 m2 g−1) and combination of carbon with nitrogen. Therefore, tubular g-C3N4 demonstrated a good specific capacitance of 233 F g−1 at a current density of 0.2 A g−1 in 6 M KOH electrolyte. Furthermore, tubular g-C3N4 maintained a high capacitance retention capability (90%) after 1000 cycles. The photocatalytic activity of tubular g-C3N4 was evaluated using the organic dyes such as Methylene Blue (MB) and Methylene Orange (MO) under visible light. Tubular g-C3N4 demonstrated good photocatalytic activity and enhanced stability compared to bulk g-C3N4. The enhanced performance is because of the high surface area, which contains more active sites for reaction. The encouraging performance of tubular g-C3N4 in supercapacitors and as a photocatalyst points toward it being a prospective material for energy storage that is environmentally clean.

The influenza virus (IV) is still of great importance as it poses an imminent threat to humans and animals. Among the three IV-types (A, B, and C) influenza A viruses are clinically the most important being responsible for severe epidemics in humans and domestic animals. Aerosol droplets transmit the virus that causes a respiratory disease in humans that can lead to severe pneumonia and ultimately death. The high mutation rate combined with the high replication rate allows the virus to rapidly adapt to changes in the environment. Thereby, IV escape the existing immunity and become resistant to drugs targeting the virus. This causes annual epidemics and demands for new compositions of the yearly vaccines. Furthermore, due to the nature of their segmented genome, IV can recombine segments. This can eventually lead to the generation of a virus with the ability to replicate in humans and with novel antigenic properties that can be the cause of a pandemic outbreak. For its propagation the virus binds to the target cells and enters the cell to replicate its genome. Newly produced viral proteins and genomes are packaged at the cell membrane where progeny virions are released. As all viruses IV depends on cellular functions and factors for their own propagation, and therefore intensively interact with the cells. This dependency opens new possibilities for anti-viral strategies