Oxy-gone in a tandem: A catalytic system composed of metal nanoparticles (NPs) and a functionalized Brønsted acidic ionic liquid (IL), both of which are immobilized in a nonfunctionalized IL, is highly efficient in upgrading lignin-derived phenolic compounds into alkanes; the hydrogenation and dehydration reactions take place in tandem.

Prussian blue analogues (PBAs) with unique three-dimensional (3D) open metal framework structure and easily adjustable composition have been widely used in oxygen evolution reaction (OER) under alkaline conditions. Herein, disintegrative...

Abstract The icing of the overhead aluminum conductor has caused the conductor load to be too heavy or uneven, which results in huge accidents. The super-lubricated surface (SLIPS) shows great potential in anti-icing. Glaze ice is a common type of icing, and its damage to transmission lines is the most serious. However, the properties and influencing factors of anti-icing lubricated surfaces at glaze ice surroundings are rarely reported. In this study, the super-lubricated surface was prepared by the anodic oxidation method, and the anti-icing properties and influencing factors of surfaces were investigated in glaze ice surroundings. The results demonstrate that the SLIPS can decrease the icing amount, which is only 41% of the original aluminum surface. SLIPS exhibits excellent anti-icing performance in different environments temperatures and rainfalls. This study provides experimental guidance for the practice application of SLIPS in anti-icing aluminum conductors.

Layered double hydroxides (LDHs) are a class of two-dimensional anionic clays with adjustable structure, which have certain corrosion resistance. However, smooth growth path of LDHs nanosheets perpendicular to the substrate limits its application in the field of corrosion. Graphene oxide (GO) possess a high specific surface area and barrier properties, which provides a promising method for further improving the corrosion resistance of LDHs. In this work, we prepared three different concentrations of sodium dodecylbenzene sulfonate (SDBS) modified GO (GO:SDBS concentration ratio = 1:1, 1:2, 1:3), and present MgAlCe-LDHs@GO-SDBS composite coatings by one-step hydrothermal method with well-zigzag morphology and good corrosion resistance. GO-SDBS was successfully incorporated in the layered double hydroxide (LDHs), the corrosion current density of the MgAlCe-LDHs@GO-S2 coatings was 1.60 × 10−8 A cm−2, which was lower than other coatings. This one-step growth of MgAlCe-LDHs@GO-S method has potential applications in manufacture of anti-corrosion protection coatings.

Fine-grained tungsten heavy alloys (WHAs) with a non-equiatomic Ni5.5Fe2.5CoCr high entropy alloy (HEA) as binder were successfully fabricated through spark plasma sintering (SPS). The influence of binder content and composition on the microstructure and mechanical properties of WHAs were systematically investigated. The average W grain size and W-W contiguity decreased with increasing Ni5.5Fe2.5CoCr content. The Ni5.5Fe2.5CoCr binder inhibited the growth of tungsten grains, resulting in finer tungsten grains (3.5±1.5 μm) in the 90W-Ni5.5Fe2.5CoCr alloy than in the conventional 90W-7Ni-3Fe alloy. This alloy showed an excellent tensile strength of 1392±33 MPa. The high strength is achieved through the synergistic effect of fine-grain strengthening, twinning strengthening, dispersion strengthening and solid-solution strengthening. In contrast, WHAs using equiatomic NiFeCoCr as binder showed lower tensile strength (540±26 MPa), caused by the formation of brittle μ phase in the binder phase. This work provides a pathway for utilizing the non-equiatomic HEA as a binder in the development of high-strength WHAs, thereby expanding their application prospects.

An ultrahigh corrosion resistance of Mg-Er alloys was achieved via a simple method by forming an Er2O3 oxide film using a high temperature treatment. The corrosion rate of Mg-8.1 wt% Er alloy with oxide film is only 0.12 mm/y in 3.5 wt% NaCl solution, even lower than that of high-purity magnesium. The triangular prism-like Mg(OH)2 was observed for the first time in corrosion field of Mg alloys, which was terrific compact and effectively hindered the further corrosion. A mechanism of two-layer barrier coming from the oxide film and triangular prism-like Mg(OH)2 was proposed to contribute the outstanding corrosion resistance.