Crystallization behavior of melt-blended polypropylene (PP)/single wall carbon nanotube (SWNT) composites has been studied using optical microscopy and differential scanning calorimetry. Polypropylene containing 0.8 wt% SWNT exhibits faster crystallization rate as compared to pure polypropylene. PP/SWNT fibers have been spun using typical polypropylene melt spinning conditions. The PP crystallite orientation and the SWNT alignment in the fibers have been studied using X-ray diffraction and polarized Raman spectroscopy, respectively.

Poly(p-phenylene benzobisoxazole) (PBO) has been synthesized in the presence of single-wall carbon nanotubes (SWNTs) in poly(phosphoric acid) (PPA) using typical PBO polymerization conditions. PBO and PBO/SWNT lyotropic liquid crystalline solutions in PPA have been spun into fibers using dry-jet wet spinning. The tensile strength of the PBO/SWNT fiber containing 10 wt % SWNTs is about 50% higher than that of the control PBO fibers containing no SWNTs. The structure and morphology of these fibers have been studied.