Substituting Salt for Cerium Oxide The water-gas shift reaction converts carbon monoxide and water to hydrogen and carbon dioxide. Catalysts that operate at lower temperatures will be useful in fuel cells. Nanoparticles of platinum adsorbed on reducible oxides, such as ceria, can stabilize catalytically active Ptoxygen species. Zhai et al. (p. 1633 ) now show that, when alkali atoms are added, atomically dispersed Pt can be an active catalyst for the water-gas shift reaction at ∼100°C, even on simple oxides such as alumina and silica.

Abstract The formamidinium lead iodide (FAPbI 3 ) perovskite has emerged as a promising material for high‐efficiency photovoltaic applications. Although a power conversion efficiency of more than 26% has been achieved, stability issues have hindered its commercial application. In this study, the stability of FAPbI 3 under adverse conditions such as humidity, oxygen, ultraviolet light, and temperature fluctuations is systematically reviewed. The known effective strategies for improving stability are discussed. Current studies have shown that technologies such as doping, halide alloying, additive manufacturing engineering, and interface modification have been identified as effective in mitigating phase transitions of FAPbI 3 and enhancing environmental durability. Encapsulation technology further improves moisture and heat resistance. Compared with other stabilization strategies, doping and alloying can address the adverse effects of narrowing of the absorption edge. Interface engineering has an essential understanding of the stability mechanism, which will greatly improve the stability problem in the practical application of FAPbI 3 . This paper also looks forward to the future research directions and development trends.