Abstract Developing a feasible and efficient separation membrane for the purification of highly emulsified oily wastewater is of significance but challenging due to the critical limitations of low flux and serious membrane fouling. Herein, a biomimetic and superwettable nanofibrous skin on an electrospun fibrous membrane via a facile strategy of synchronous electrospraying and electrospinning is created. The obtained nanofibrous skin possesses a lotus‐leaf‐like micro/nanostructured surface with intriguing superhydrophilicity and underwater superoleophobicity, which are due to the synergistic effect of the hierarchical roughness and hydrophilic polymeric matrix. The ultrathin, high porosity, sub‐micrometer porous skin layer results in the composite nanofibrous membranes exhibiting superior performances for separating both highly emulsified surfactant‐free and surfactant‐stabilized oil‐in‐water emulsions. An ultrahigh permeation flux of up to 5152 L m −2 h −1 with a separation efficiency of >99.93% is obtained solely under the driving of gravity (≈1 kPa), which was one order of magnitude higher than that of conventional filtration membranes with similar separation properties, showing significant applicability for energy‐saving filtration. Moreover, with the advantage of an excellent antioil fouling property, the membrane exhibits robust reusability for long‐term separation, which is promising for large‐scale oily wastewater remediation.

Single-wall carbon nanotubes (SWCNTs) are ideal for fabricating transparent conductive films because of their small diameter, good optical and electrical properties, and excellent flexibility. However, a high intertube Schottky junction resistance, together with the existence of aggregated bundles of SWCNTs, leads to a degraded optoelectronic performance of the films. We report a network of isolated SWCNTs prepared by an injection floating catalyst chemical vapor deposition method, in which crossed SWCNTs are welded together by graphitic carbon. Pristine SWCNT films show a record low sheet resistance of 41 ohm □-1 at 90% transmittance for 550-nm light. After HNO3 treatment, the sheet resistance further decreases to 25 ohm □-1. Organic light-emitting diodes using this SWCNT film as anodes demonstrate a low turn-on voltage of 2.5 V, a high current efficiency of 75 cd A-1, and excellent flexibility. Investigation of isolated SWCNT-based field-effect transistors shows that the carbon-welded joints convert the Schottky contacts between metallic and semiconducting SWCNTs into near-ohmic ones, which significantly improves the conductivity of the transparent SWCNT network. Our work provides a new avenue of assembling individual SWCNTs into macroscopic thin films, which demonstrate great potential for use as transparent electrodes in various flexible electronics.

Excessive use of veterinary drugs causes severely environmental pollution and agricultural pollution, and poses great threat to human health. A simple method for the rapid, highly sensitive, and on-site monitoring of veterinary drug residues in complex samples remains lacking.